Magnetic Properties and GMR of Sputtered Permalloy/Au Multilayers |
| B. Szymański and F. Stobiecki Institute of Molecular Physics, Polish Academy of Sciences, Smoluchowskiego 17, 60-179 Poznań, Poland |
| Full Text PDF |
| We report on structural, magnetic, and GMR properties of permalloy/Au multilayers where permalloy = Ni83Fe17, deposited by face-to-face sputtering onto Si(111) substrate. X-ray diffraction studies confirmed a good structural quality of our multilayers. The samples were characterised with vibrating sample magnetometer, longitudinal magnetooptical Kerr effect and giant magnetoresistance measurements. It was determined that our multilayers are magnetically very soft with Hc ≈ 1 Oe and show uniaxial anisotropy with HK ≈ 5 Oe. For gold sublayer thickness dAu close to 1.1 nm the antiferromagnetic coupling is present in very narrow Au thickness range (≈ 0.2 nm). Despite a good structural quality of samples relatively small giant magnetoresistance value (1.2% at room temperature) was found. It is due to non-perfect aniferromagnetic coupling caused by pinholes. |
| DOI: 10.12693/APhysPolA.97.535 PACS numbers: 75.70.-i, 75.70.Pa, 68.55.-a |