Magnetic Properties of Nanocrystalline Co/Ti and Co/Zr Multilayers
L. Smardza and K. Smardzb
a Institute of Molecular Physics, Polish Academy of Sciences, Smoluchowskiego 17, 60-179 Poznań, Poland
b Institute of Mater. Sci. and Eng., University of Technology Pl. Curie 5, 60-965 Poznań, Poland
Full Text PDF
It is shown that the Co sublayers grow in the soft magnetic nanocrystalline phase up to a critical thickness d≈3 and 2.8 nm for Co/Ti and Co/Zr MLs, respectively. The rapid decrease in the interlayer exchange coupling could be explained by its strong damping due to formation of a non-magnetic quasi-amorphous Co-Ti and Co-Zr alloy layer at the interfaces. The nanocrystalline 2.2 nm-Co/2 nm-Ti ML shows a weak 90° coupling near the transition zone from ferromagnetic to zero coupling.
DOI: 10.12693/APhysPolA.97.511
PACS numbers: 75.70.-i, 75.30.Et